Evolution of Contact Damage in Layer Structures. Brittle layer structures (eg brittle coating on ceramic substrate) can be much more damage tolerant than their constituent material components - cracks tend to remain contained within the coating. Very little is known about the factors that control this behaviour. This project will exploit unique local expertise in modelling damage evolution to fill a niche in a large study being carried out at the National Institute of Standards (NIST) in the U ....Evolution of Contact Damage in Layer Structures. Brittle layer structures (eg brittle coating on ceramic substrate) can be much more damage tolerant than their constituent material components - cracks tend to remain contained within the coating. Very little is known about the factors that control this behaviour. This project will exploit unique local expertise in modelling damage evolution to fill a niche in a large study being carried out at the National Institute of Standards (NIST) in the U.S.A. An understanding of the factors that maximise the containment of cracks is essential to the design and development of the next generation of advanced layer composites for many biomechanical and other engineering applications.Read moreRead less
Boundary Effects on Bridging-Stress/Crack-Opening Relationship and Specific Fracture Energy. This project is to investigate the boundary/interface influence on fracture/material properties of composites and thin layered structures along crack path to free boundary and bi-material interface. The local fracture energy dissipation along crack path is emphasised and used to study the boundary influence on the cohesive law - the relationship between crack bridging stress and crack opening displaceme ....Boundary Effects on Bridging-Stress/Crack-Opening Relationship and Specific Fracture Energy. This project is to investigate the boundary/interface influence on fracture/material properties of composites and thin layered structures along crack path to free boundary and bi-material interface. The local fracture energy dissipation along crack path is emphasised and used to study the boundary influence on the cohesive law - the relationship between crack bridging stress and crack opening displacement. New fracture mechanics model is proposed that incorporates the boundary/interface influence and the more popular size effect. The new boundary/interface effect model will be more relevant to modern materials applications related to layered ceramics, thin films, coatings in electronic and bio-medical applications.Read moreRead less